Facile fabrication, mechanical property and flame retardancy of aerogel composites based on alginate and melamine-formaldehyde

期刊

POLYMER
卷 181, 期 -, 页码 -

出版社

ELSEVIER SCI LTD
DOI: 10.1016/j.polymer.2019.121783

关键词

Water resistant; Flame retardant; Aerogel

资金

  1. Science Challenge Project [TZ2018004]
  2. National Science Foundation of China [21707127, 21504071]

向作者/读者索取更多资源

Aerogel composites based on melamine-formaldehyde (MF) and alginate (A) was fabricated with ice-templated method. The preparation process involves two cross-linking processes, in aerogel precursor at room temperature and in dried aerogel at 80 degrees C (100% humidity), respectively. Cross-linking was demonstrated to be very efficient for improving the mechanical property and water resistance of MF-A aerogels. The obtained aerogels have compressive moduli ranging from 1.2 MPa to 24.1 MPa. All the cross-linked aerogels display good dimensional stability when soaked in water. The morphological study of MF-A aerogels show a layered or network microstructure, with a homogeneous distribution of MF spheres. Due to low density and porous structure, MF-A aerogels have low thermal conductivity from 0.035 to 0.047 W/m K. MF-A aerogels have good thermal stability and extremely low flammability, with LOI value up to 41%. This novel aerogel from partially bio-based raw material would have promising application prospects.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据