Gd-Co nanoferrite; Coercive field; Microwave absorption; Rare earths
资金
- Research Council of the University of Yasouj [Gryu-89131107]
In this work, neodymium substituted gadolinium-cobalt ferrite nanoparticles were synthesized by hydrothermal method. The significant role of doping both the Nd3+ and Gd3+ ions to cobalt ferrite in manipulating the cation distribution and further in influencing structural and magnetic properties was experimentally studied and reported. The influence of Nd3+ substitution was investigated with step of 0.02-0.1 into the optimized Gd-Co compound. The crystal structure formation and crystallite size were explored by X-ray diffraction analysis in which the crystallite size and lattice constant decrease with increasing the Nd3+ substitution. The microstructural properties were studied by field emission scanning electron microscopy and atomic force microscopy studies. The obtained structural and morphological results reveal that the substitution of Nd3+ with more than 0.06 into the Gd-Co ferrites will change the material behavior and trends. The saturation magnetization and coercivity values were measured using a vibration sample magnetometer at room temperature. Comparative microwave absorption experiments demonstrate that the reflection loss properties enhance with increasing substitution of Nd3+ cations in Gd-Co ferrite spinet structure. This research reports that the as-prepared Nd3+ substituted Gd-Co ferrite compound stands as promising candidate for absorbing electromagnetic wave with a wider absorbing bandwidth of X-band. (C) 2020 Chinese Society of Rare Earths. Published by Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据