期刊
JOURNAL OF PROSTHETIC DENTISTRY
卷 124, 期 1, 页码 81-86出版社
MOSBY-ELSEVIER
DOI: 10.1016/j.prosdent.2019.09.002
关键词
-
资金
- Vice-Chancellery of Shiraz University of Medical Sciences [1957]
Statement of problem. Digital systems have been developed as substitutes for the traditional fabrication of wax patterns and definitive restorations, but the accuracy of these systems is unclear. Purpose. The purpose of this in vitro study was to evaluate and compare the marginal fit of metal copings fabricated from milling, stereolithography (SLA), and 3D wax printer (PolyJet) patterns. Material and methods. A standard machined brass die model was designed and prepared. To fabricate metal copings of standardized shape and dimensions, the die was scanned and nickel-chromium (Ni-Cr) copings were designed by using a dental designer software program. By using the same CAD data to fabricate 30 patterns through milling, SLA, and PolyJet techniques, 10 resin patterns were milled by using a 5-axis milling machine, 10 resin patterns were produced by using a NextDent 5100 3D Printer, and 10 wax patterns were printed by using a Solidscape 3D printer. The patterns were invested and cast in Ni-Cr alloy. Each coping was evaluated by using a digital microscope on 16 points around the finish line on the metal die at x230 magnification. The mean marginal discrepancy was calculated. The mean differences among the groups were compared by using 1-way ANOVA, and post hoc analysis was used for pairwise comparison of the groups (alpha=.05). Results. The mean value of marginal discrepancy was 93.1 +/- 25 mm in the milling, 71.1 +/- 25 mm in the SLA, and 41.3 +/- 6 mm in the PolyJet group. No statistically significant difference was found between the milling and SLA groups (P=.158), while the PolyJet group showed significantly lower mean marginal discrepancy than the 2 other groups (P<.05). Conclusions. The PolyJet method produces metal copings with better marginal fit than the SLA or milling techniques. However, the marginal fit was clinically acceptable in metal copings made with all the 3 methods.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据