期刊
JOURNAL OF POWER SOURCES
卷 438, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2019.227042
关键词
Biogas; Efficient anode; Nanocomposite; Fuel cell performance
资金
- Higher Education Commission of Pakistan (HEC)
This paper describes the fabrication of Ni0.6Zn0.4-Gd0.2Ce0.8O2-delta (NiZn-GDC) via a two-step wet chemical synthesis technique. This composite was found to be more thermally stable and carbon resistive under the intense reducing environment of biogas. This was confirmed by different characterization techniques. The maximum power density P-max, was achieved at 600 degrees C as 820 mW/cm(2) and 548 mW/cm(2) with hydrogen and biogas, respectively. Different characterization techniques have been performed, such as X-ray diffractometry (XRD), scanning electron microscopy (SEM/EDX), UV visible spectroscopy, and Raman spectroscopy. The XRD pattern by Rietveld refinement showed two-phase structures of the anode composite with an average crystallite size of 25 35 nm before and after reduction with methane. The optical band gap (E-g(opt)) of NiZn-GDC was calculated to be 2.24eV from the Tauc plot using absorbance data. The Nyquist plot was also drawn to study the AC electrochemical impedance spectra (EIS) of the nanocomposite anode from 450 degrees C to 600 degrees C in air. The maximum DC conductivity of 1.37 S/cm was observed at a temperature of 600 degrees C using the four-probe DC technique.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据