期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 818, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2019.152891
关键词
Magnesium alloys; Formability; Plastic anisotropy; Texture; Second phase particles
资金
- Japan Society for the Promotion of Science (JSPS) [16H04525]
- Grants-in-Aid for Scientific Research [16H04525] Funding Source: KAKEN
Effects of scandium (Sc) content on microstructures and mechanical properties of a Mg-1.5Zn (wt.%) alloy have been systematically investigated. Mg-1.5Zn alloys with Sc content no more than 0.3 wt% showed large index Erichsen (I.E.) values, an indicator of stretch formability, over than 8 mm due to weak basal textures. Further increase in Sc content up to 1.5 wt% led to a gradual decline in the stretch formability and a Mg-1.5Zn-1.5Sc alloy showed the lowest I.E. value of 4.2 mm. Detailed microstructural characterization of the Mg-1.5Zn-1.5Sc alloy revealed that the poor stretch formability was associated with a combined effect of strong basal texture, un-recrystallized matrix grains and a dense distribution of ScZn and Sc second phase particles. On the other hand, tensile properties, in particular tensile yield strength (TYS) and r-value were almost identical along the rolling direction (RD) and the transverse direction (TD) for a Mg-1.5Zn-0.1Sc alloy. Higher TYS and r-value along the RD than the TD were observed in a Mg-1.5Zn-0.3Sc alloy, while opposite results were obtained in Mg-1.5Zn-1.0Sc and Mg -1.5Zn-1.5Sc alloys. Different plastic anisotropy trends observed in Mg-1.5Zn-xSc (x = 0.1-1.5) alloys could be ascribed to their distribution of crystallographic orientations. (C) 2019 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据