期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 811, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2019.152006
关键词
Electrodeposition; Multilayers; Oxidation; Ni-Co-Mn
资金
- China Scholarship Fund
- Jiangsu University of Science and Technology [1624821607-5]
- Priority Academic Program Development of Jiangsu Higher Education Institutions
In order to obtain the high conductivity values and wide spinel stability region for solid oxide fuel cell interconnect, several multilayer Ni, Co and Mn coatings are electroplated and then oxidized in air to form spinel oxide layers. Potentiodynamic polarization curves in different simple solutions are tested to analyze the deposition behavior of Co and Mn. Microstructures and compositions of Ni-Co-Mn multilayers by adjusting the thickness and deposition parameters are analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that area specific resistance value of sample B-Ni/Co after oxidation at 750 degrees C for 500h is the lowest among the coatings, and the resistance values at 700 degrees C and 800 degrees C are 35.3 and 31.7 m Omega.cm(2), respectively. When the Ni transition layer in the vicinity of coating/substrate interface is thick, it will lead to the outward diffusion and aggregation of element Fe to form Ferich oxide intermediate layer, which will affect the high-temperature performance of the coating. Pure Co and CoMn alloy coatings with a certain thickness can effectively prevent the inward diffusion of oxygen and the outward diffusion of Fe and Cr at high temperature. The thin Ni transition layer combined with the thick Co layer or CoMn layer has the best element diffusion inhibition and high temperature electrical properties during the long-term high-temperature oxidation process. (C) 2019 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据