期刊
ENGINEERING FRACTURE MECHANICS
卷 220, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.engfracmech.2019.106661
关键词
Fatigue crack initiation; Corrosion morphology; Crystal plasticity modeling; X-ray computer tomography; Microstructure
类别
资金
- Office of Naval Research [N00014-14-1-0544, N00014-14-1-0012]
The onset of fatigue crack initiation is driven by the microstructure and the corrosion morphology; however, these mechanisms are rarely studied synergistically. In this work, characterizations of the microstructural features and the corrosion morphology resulting from two different environmental exposures are instantiated into crystal plasticity models. Fatigue indicator parameters (FIPs) are calculated from the micromechanical fields to quantify failure. The FIPs compare favorably to predict the experimentally observed location of fatigue crack initiation. These results show the potential behind analyzing environmentally-assisted fatigue crack initiation from a multivariable perspective.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据