Coating; SiC; Ablation; Erosion; Reactive melt infiltration; Graphite
In this study, chemical and mechanical erosion mechanism of SiC single-layer coatings were evaluated using supersonic flame erosion test, X-ray diffraction, and scanning electron microscopy. In the first step, the formation mechanism of SiC coating on graphite substrate was investigated by HSC Chemistry software version 6.0 and then the effects of infiltration temperature and SiC nanoparticles addition on erosion behavior of the coatings were studied. The results of erosion test under supersonic flame at a 90 degrees angle after 120 s indicated that chemical and mechanical erosion occur simultaneously during erosion test but mechanical erosion is the dominant mechanism which causes to sample destruction. However, with SiC nanoparticles addition and increasing the infiltration temperature, mechanical erosion decreased. By increasing of infiltration temperature, mass erosion rate and linear erosion rate decreased from 2.52 x 10(-3) g cm(-2) s(-1) and 32.7 mu m s(-1) to 1.09 x 10(-3) g cm(-2) s(-1) and 3.33 mu m s(-1) respectively. Also, with addition of SiC nanoparticles, mass and linear erosion rate decreased from 2.52 x 10(-3) g cm(-2) s(-1) and 32.7 mu m s(-1) to 1.04 x 10(-3) g cm(-2) s(-1) and 2.17 mu m s(-1) respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据