Differential Polymorphic Transformation Behavior of Polybutene-1 with Multiple Isotactic Sequences

期刊

CHINESE JOURNAL OF POLYMER SCIENCE
卷 38, 期 2, 页码 164-173

出版社

SPRINGER
DOI: 10.1007/s10118-020-2337-6

关键词

Polybutene-1; Polymorphic transformation; Isotactic sequence; Crystallinity; Lamellae thickness

资金

  1. Key R&D Program (Major Scientific and Technological Innovation Project) of Shandong Province
  2. Natural Science Foundation of Shandong Province [ZR2019MB072]
  3. Taishan Scholar Program

向作者/读者索取更多资源

For the solid-solid transformation from form II to form I of isotactic polybutene-1 (iPB), the temperature dependence of form I nucleation and growth was deemed to control the transformation process. However, the relationship between form I formation and form II disappearance in the transformation process is not clear. In this work, the spontaneous crystal transformation from form II to I of iPB with 81 mol% mmmm sequence concentration is studied firstly by tracking the two processes, the decay of form II and the yielding of form I in a wide range of temperature spanning from 0 degrees C to 50 degrees C and in a long transformation time ranging from 5 min to 65 days with in situ FTIR and WAXD. Unlike the literature reports, the decay rate of form II is firstly found to be lower than the yielding rate of form I at all studied temperatures, especially at low transition temperature. This is attributed to the amorphous chains which locate near crystal lamella participating into the nucleation of form II. The regular chain folding and growth of iPB form I from amorphous chains containing short isotactic sequences also lead to an increase in crystallinity of form I compared with that of initial form II crystallized at 60 degrees C. An increase in the annealing temperature results in decrease in crystallinity and increase in lamellae thickness of iPB form I.