期刊
CATALYSIS TODAY
卷 353, 期 -, 页码 53-62出版社
ELSEVIER
DOI: 10.1016/j.cattod.2019.10.028
关键词
Guard bed; Silicon; NiMo; Alumina; Hydrotreating
资金
- Government assignment of Russian Federation by Boreskov Institute of Catalysis [AAAA-A17-117041710077-4]
The influence of alumina precursors on NiMo/gamma-Al2O3 catalysts for silicon removal from gas oil have been studied. Alumina precursors were prepared by hydrothermal treatment of gibbsite, precipitation of aluminum nitrate by ammonia and precipitation of aluminum nitrate in autoclave. Alumina precursors, supports and catalysts were studied by XRD, nitrogen adsorption-desorption, IR spectroscopy, UV-vis, XPS, SEM, HRTEM. Series of NiMo/gamma-Al2O3 catalysts differed in preparation method of alumina precursors was tested in hydrotreating of diesel fraction contaminated with decamethylcyclopentasiloxane as a model silicon compound. It was shown that prepared alumina precursors were boehmites and dawsonite, which had different particle size. The supports prepared from these alumina precursors were gamma-Al2O3 with different particles size. It was shown that there was a dependence of the surface area of the support on the size of primary particles measured by XRD. The higher surface area results in the higher content of OH groups and silicon sorption capacity. Morphology of the sulfide active component also depends on the size of primary particles. The higher length of the particles, the higher slab length of NiMoS phase. The catalyst with the lowest particle size of alumina and highest length of active component had the highest HDS activity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据