DOI: 10.3390/met9090941
关键词
Al-Zn-Mg-Cu alloy; microstructure evolution; superplastic
资金
- National Science Foundation of China [51334006]
The microstructural evolution of the Al-Zn-Mg-Cu alloy during the superplastic deformation process has been studied by high temperature tensile experiment. The superplastic deformation behaviors are investigated under different temperatures of 470 degrees C, 485 degrees C, 500 degrees C, 515 degrees C and 530 degrees C, and different strain rates of 3 x 10(-4) s(-1), 1 x 10(-3) s(-1), 3 x 10(-2) s(-1) and 1 x 10(-2) s(-1). The microstructure observation shows that uniform and equiaxed grains can be obtained by dynamic recrystallization in the initial stage of superplastic deformation. Once the recrystallization process has been finished, the variations of the fraction of high angle boundary, the grain aspect ratio and the Schmid factor are negligible during the superplastic deformation, which shows that the grain boundary sliding and grain rotation are the main deformation mechanisms. The maximum texture intensity decreases compared with the initial microstructure, indicating that grain boundary sliding and grain rotation can weaken the texture, however, the texture intensity increases in the final stage of superplastic deformation, which may be resulted from the stress concentration.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据