RADIATION PHYSICS AND CHEMISTRY
卷 161, 期 -, 页码 55-59出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.radphyschem.2019.04.019
关键词
Hardox-450 and Hardox HiTuf steels; Boronizing; Radiation shielding; Mass attenuation coefficient; Effective atomic number; Mean free path
资金
- Harran University Scientific Research Council (HUBAK) [17044]
In this work, the variation with boronizing process of radiation shielding properties of Hardox 450 and Hardox HiTuf steels was studied. Some radiation shielding parameters as mass attenuation coefficient (MAC), linear attenuation coefficient (LAC), half value layer (HVL), tenth layer value (TVL) and mean free part (MFP) of the steel samples were measured before and after boronizing. Also, the boronizing temperature effect on the radiation shielding was investigated for the heated samples at 800, 900 and 1000 degrees C. The radiation shielding parameters were determined at photon energy range of 80.99-778.90 keV. The experimental results were compared with the theoretical values obtained from WinXCom program, and good agreements were observed between the values of MAC before boronizing (H0 and HH0). It is observed that the values of MAC have increased with the increasing temperature and the best absorption is observed for the samples heated at 1000 degrees C. The results show that the gamma rays more shielded effectively with boronizing process in steel samples and boronizing and temperature effect on the absorption of Hardox-HiTuf steel is more than Hardox 450.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据