MICROPOROUS AND MESOPOROUS MATERIALS
卷 284, 期 -, 页码 316-326出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.micromeso.2019.04.041
关键词
Hierarchical ZSM-5; Zn modification; Ethylene aromatization; Alkali treatment
类别
资金
- KRICT Big Project Program [SI1801-06]
- Cl Gas Refinery Program - Ministry of Science, ICT & Future Planning [2015M3D3A1064901]
- Korea-China collaboration program from the State Key Laboratory of Materials- Oriented Chemical Engineering. China [KL17-08]
A series of Zn modified hierarchical ZSM-5 catalysts with Si/Al ratios of 25 and 40, and Zn loading amounts of 0, 0.5, 1, and 2 wt% was designed to pursue a highly efficient catalyst with excellent catalytic activity and stability toward BTEX formation in the aromatization of light hydrocarbons. The Zn modified hierarchical ZSM-5 catalysts with intracrystalline mesopores were prepared by alkali treatment and Zn impregnation. The effects of the alkali treatment and Zn modification on the textural property, acidity, catalytic performance, and coke formation were investigated in detail via various characterization techniques. It was found that the catalytic stability of the alkali-treated catalysts notably improved. This can be mainly attributed to the fact that the alkali treatment of the pre-synthesized ZSM-5 generated a large amount of mesopores, which could alleviate the diffusion limitations. Moreover, the Zn modification remarkably improved the initial BTEX yield, which was due to the improved Lewis/Bronsted (L/B) ratio in the prepared catalysts. However, as the Zn loading amount increased from 0 to 2 wt%, the catalyst stability dramatically decreased, especially for the 2 wt% case. It seems that the balance between the Lewis and Bronsted acid sites (i.e., the suitable L/B ratio) is the key to obtaining both high BTEX yield and catalyst stability, and the optimum Zn loading amount is determined to be 0.5 wt% with an L/B ratio of around 1.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据