期刊
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY
卷 140, 期 1, 页码 283-293出版社
SPRINGER
DOI: 10.1007/s10973-019-08809-1
关键词
Copolymerized PMIA; Pyrolysis; Activation energy; Kinetics
资金
- Fundamental Research Funds for the Central Universities
- Graduate Student Innovation Fund of Donghua University [CUSF-DH-D-2019012]
- Shanghai International S&T Cooperation Fund [16160731302]
- Natural Science Foundation of China [51473031]
Copolymerized poly(m-phenylene isophthalamide) (co-PMIA) was synthesized by solution polycondensation using m-phenylenediamine and isophthaloyl dichloride and 3,4 '-oxydianiline (3,4 '-ODA). This paper described the preparation and characterization of the copolymers from various contents 3,4 '-ODA to afford co-PMIA with ideal high molecular mass. The copolymer showed excellent thermal stability with the glass transition temperature of 267 degrees C and the onset decomposition temperature (5% mass loss) of 445 degrees C. The thermal degradation of co-PMIA was measured with various thermal analytical techniques; the pyrolysis products were obtained and analyzed under air atmosphere. The possible thermal decomposition mechanism of co-PMIA was discussed. The present pyrolysis was investigated using TG under air atmosphere at four different heating rates (5-20 degrees C min(-1)). Three different kinetic methods, the iso-conversional Ozawa-Flynn-Wall and Kissinger and Crane methods were applied on TG data of co-PMIA to calculate the kinetic parameters including activation energy, pre-exponential factor and reaction order.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据