期刊
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
卷 35, 期 8, 页码 1578-1586出版社
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/j.jmst.2019.04.008
关键词
Selective laser melting; Ti-6Al-4V; Microstructure; Heat treatment
资金
- Monash Centre for Additive Manufacturing (MCAM)
- Australia Research Council [IH130100008]
- National Natural Science Foundation of China [51701124]
- Australian Research Council [LE0882821]
Static coarsening mechanism of selective laser melted (SLMed) Ti-6Al-4V with a lamellar microstructure was established at temperatures from 700 degrees C to 950 degrees C. Microstructure evolution revealed that high heat treatment temperature facilitated martensite decomposition and promoted lamellae growth. At each temperature, the growth rate decreased with increasing holding time. The static coarsening behaviour of SLMed Ti-6Al-4V can be interpreted by Lifshitz, Slyozov, and Wagner (LSW) theory. The coarsening coefficient were 0.33, 0.33-0.4, 0.4-0.5 for 700-800 degrees C, 900 degrees C and 950 degrees C, respectively. This indicated the coarsening mechanism was bulk diffusion at 700-800 degrees C, and a combination of bulk diffusion and interface reaction at 900 degrees C and 950 degrees C conditions. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据