期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 802, 期 -, 页码 364-372出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2019.06.174
关键词
Multiwalled carbon nanotube; EM wave absorption; Dielectric loss; Magnetic loss; Impedance matching
资金
- National Natural Science Foundation of China [61701185, 61801186, 61605147]
In this study, multiwalled carbon nanotube (MWCNT) anchored on the surface of silica coated porous rodlike nickel ferrite (NiFe2O4@SiO2) composite was fabricated, and its structure, composition, magnetic and electromagnetic (EM) wave absorption properties were studied. High-performance EM wave absorption properties of the ternary composite can be regulated by the coating thickness and the content of the absorber. The reflection loss (RL) was optimized to -67.8 dB at the matching thickness of 1.9 mm, and the effective absorption bandwidth (RL <= -10 dB) was 4.5 GHz (13.5-18 GHz) at the coating thickness of only 1.5 mm with the filler loading 40 wt%. The effective bandwidth can reach 5.3 GHz (12.7-18 GHz) at the coating thickness of only 2.2 mm with the filler loading 30 wt%. The broadband absorption, thin thickness, strong absorption and adjustable absorption properties endow NiFe2O4@SiO2/MWCNT composite with extensive prospects for EM wave absorption. (C) 2019 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据