INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY
卷 17, 期 1, 页码 285-295出版社
WILEY
DOI: 10.1111/ijac.13344
关键词
aluminum nitride; tape casting; thermal conductivity; viscosity
资金
- Special Fund of Shanghai Committee of Science and Technology for Local University [14520500300]
Aluminum nitride (AlN) ceramic substrates have been fabricated using non-aqueous tape casting and pressureless densification under flowing N-2 atmosphere. Considering the economic and environmental impact, a new strategy of solvent and dispersant system was adopted to prepare AlN slurries with high solid loading. According to the viscosity characteristics of AlN slurries, dispersant content was adjusted to be 0.5 wt% of AlN powder in order to optimize the rheological behavior of AlN slurries. The addition contents of binder and plasticizer were both optimized as 5 wt% of AlN powders by combining the viscosity of slurries and tensile strength of green tapes. Green AlN tapes were fabricated with an optimized tape casting process such as dry temperature. The exclusion process of organic additives was investigated by employing thermogravimetric analysis. Flat and dense AlN ceramic substrates with a relative bulk density over 99.75 % were achieved after being sintered under 1800 degrees C for 6 hours, which had a maximum size of 110 x 110 mm. The thermal conductivity of the AlN substrate could reach 145 Wm(-1)K(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据