期刊
ACS NANO
卷 13, 期 9, 页码 10376-10385出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsnano.9b04165
关键词
spinel nanodots; Zn-ion battery; diffusion coefficient; active surface; flexibility
类别
资金
- National Natural Science Foundation of China [51872051, 51701042]
- Science and Technology Committee of Shanghai Municipality [18520723100]
- Researching Program of State Grid Corporation of China [GYW17201800011]
Rechargeable aqueous Zn-ion batteries (ZIBs) have recently attracted much attention due to their low cost and superior safety. Unfortunately, their low capacity and poor cycle life still hinder their practical application. Here, we have developed a general synthesis strategy for ultrasmall spinel oxide nanodots (Mn3O4, CoMn2O4, MnCo2O4.5, Co3O4, and ZnMn2O4) with abundant oxygen vacancies and highly active surface. Among them, 6.0-nanometer-sized Mn3O4 nanodots deliver the best Zn-ion storage ability with a high reversible capacity of 386.7 mA h g(-1) at 0.1 A g(-1), excellent rate performance, and a long-term stability of 500 cycles at 0.5 A g(-1). Taking advantage of the highly activated surficial atoms, shortened transfer pathway, and introduction of numerous oxygen vacancies, an ultrahigh Zn2+ diffusion coefficient of 2.4 x 10-10 cm(2) has been detected during the discharge process. This value is more than 2 orders of magnitude higher than that of other spinel oxide nanostructures in previous reports and also the highest one in all of the as-reported ZIB cathode materials to date. Our finding offers promising opportunities for the development of ZIB cathode materials with high energy density, long-term cycling stability, excellent flexibility, and wearability.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据