期刊
MATERIALS RESEARCH EXPRESS
卷 6, 期 8, 页码 -出版社
IOP Publishing Ltd
DOI: 10.1088/2053-1591/ab274c
关键词
electroplating; ZnS; ZnO; thin film
资金
- Ekiti State University
- Sheffield Hallam University
The effect of deposition temperature on the material and electronic properties of ZnS layers grown using a two-electrode electroplating configuration was explored and reported. The aqueous electrolyte from which ZnS layers were deposited contains 0.2 M ammonium thiosulphate ((NH4)(2)S2O3) and 0.2 M zinc sulphate monohydrate (ZnSO4 center dot H2O). Deposition temperatures of 30 degrees C, 55 degrees C and 80 degrees C were utilised. The electroplated thin-films were deposited on glass/fluorine-doped tin oxide (FTO) substrate and characterised for their structural, optical, morphological, compositional and electrical properties using x-ray diffraction (XRD), UV-Visible spectrophotometer (Optical absorption), Scanning electron microscopy (SEM), energy-dispersive x-ray analysis (EDX), Photoelectrochemical (PEC) cell measurements and DC conductivity measurements techniques. The XRD results indicate that the electroplated ZnS layers at 30 degrees C are polycrystalline with the dominant orientation along the ZnS(111)C plane. The XRD micrograph shows the presence of ZnO and unreacted Zn diffractions and amorphisation of the ZnS layers after heat treatment. The readings and estimations made from the UV-Visible spectrophotometric data depict a transition from a bandgap of similar to 3.6 eV for the ZnS layers grown at 30 degrees C to similar to 3.1 eV for layers grown at 80 degrees C. The similar to 3.6 eV and similar to 3.1 eV obtained bandgaps correspond to the bulk bandgaps of ZnS (of similar to 3.7 eV) and ZnO (of similar to 3.7 eV), respectively. PEC cell measurements show that the grown ZnS layers are n-type and the magnitude of the PEC signal varies with an increase in the deposition temperature. The DC conductivity measurements revealed that the conductivity of the ZnS layers is between (2 and 6) x 10 (-4) Omega(-1) cm(-1). There was a gradual increase in the ZnS layer conductivity as the deposition temperature increased.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据