期刊
JOURNAL OF ADVANCED CERAMICS
卷 8, 期 2, 页码 218-227出版社
SPRINGEROPEN
DOI: 10.1007/s40145-018-0307-z
关键词
carbon fiber reinforced mullite composite; sol; mechanical property; thermal stability
资金
- Open Foundation of Science and Technology on Thermostructural Composite Materials Laboratory [614291102010117]
- Science Innovation Foundation of Shanghai Academy of Spaceflight Technology [SAST2015043]
- National Natural Science Foundation of China [11572277]
For the wide application as thermal protection materials, it is very necessary for mullite ceramics to improve fracture toughness. In this paper, the laminated and stitched carbon fiber cloth preform reinforced mullite (C/mullite) composites were prepared through the route of sol impregnation and heat treatment using the Al2O3SiO2 sol with a high solid content as raw materials. The C/mullite composites showed a flexural strength of 228.9 MPa that was comparable to that of dense monolithic mullite although the total porosity reached 13.4%. Especially, a fracture toughness of 11.2 MPam(1/2) that was 4-5 times that of dense monolithic mullite was obtained. Strength deterioration due to the carbothermal reduction between carbon fiber and the residual SiO2 in matrix was found above 1200 degrees C. A pyrolytic C (PyC) coating was deposited on carbon fibers as interfacial coating. The chemical damage to carbon fibers was obviously alleviated by the sacrifice of PyC coating. Accordingly, the C/PyC/mullite composites kept strength unchanged up to 1500 degrees C, and showed much higher strength retention ratio than C/mullite composites after annealing at 1600 degrees C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据