ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING
卷 16, 期 1, 页码 53-63出版社
SPRINGERNATURE
DOI: 10.1016/j.acme.2015.09.004
关键词
PH stainless steel; Heat treatment; Microstructure; CNC turning; Machinability
This study is an attempt to correlate the microstructure and mechanical properties of commercial 15Cr-5Ni precipitation-hardening stainless steel in different aging regimes such as solution treated (Condition A), over-aged (Condition H1150-M) and peak-aged (Condition H900) with their machinability behavior. Aging was done on 15Cr-5Ni precipitation-hardenable stainless steel samples in a temperature range of 480-760 degrees C. Over aging of the above material resulted in an improvement of ductility and a substantial reduction in tensile strength. Heat treated samples were machined in order to study the effects of machining parameters on machinability aspects such as cutting forces, surface roughness, chip morphology and tool wear. Experimental investigation revealed a strong correlation between the rate of cooling after aging and cutting forces. Air cooled samples exhibited higher cutting forces compared to furnace cooled samples. The surface finish is found to be improved for H900 air cooled sample, which has higher hardness than that of as received sample and H1150-M condition. (C) 2015 Politechnika Wroclawska. Published by Elsevier Sp. z o.o. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据