Multilayer; TiBN; CVD; TEM; Micromechanical testing
资金
- Austrian Federal Ministry for Digital and Economic Affairs
- National Foundation for Research, Technology and Development
Application of a multilayered coating architecture based on two alternating hard materials provides a strategy to enhance the mechanical properties of hard coatings for the metal cutting industry. Within this work, the mechanical behavior of CVD TiN/TiBN multilayer coatings was correlated with their microstructure and compared to the respective single-layers. Multilayers with different bilayer periods (1400, 800, 300 and 200 nm) were prepared in an industrial-scale thermal CVD plant by alternate variation of the feed gas composition. Complementary X-ray diffraction, Raman spectroscopy and transmission electron microscopy investigations confirmed a dominating face-centered cubic TiN structure, accompanied by hexagonal TiB2 and amorphous TiB in the B containing coatings. The addition of B and a decreasing bilayer period resulted in a decreasing grain size and increasing hardness. Micromechanical bending tests revealed an increase of strength and fracture toughness with addition of B and increasing layer number. While the highest strength was observed in a TiBN single layered coating, the multilayered TiN/TiBN with a bilayer period of 200 run was the hardest and at the same time toughest of the investigated coatings.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据