MOF-801; PEBA; Mixed-matrix membrane; Composite membrane; CO2/N-2 separation
资金
- National Natural Science Foundation of China [21776125, 21490585, 5171101539]
- Innovative Research Team Program by the Ministry of Education of China [IRT17R54]
- Topnotch Academic Programs Project of Jiangsu Higher Education Institutions (TAPP)
The combination of CO2-selective porous framework with polymeric material is promising for developing mixed-matrix membranes. In this work, a novel metal organic framework MOF-801 nanocrystal was introduced into polyether-block-amide (PEBA) polymer to fabricate a new mixed-matrix material for CO2 separation. A thin membrane layer consisting of MOF-801 filler and PEBA matrix was successfully formed on a porous substrate via spinning-coating approach. SEM, XRD, TGA, FTIR and adsorption test were applied to systematically characterize the as-prepared MOF-801 crystals and MOF-801/PEBA mixed-matrix composite membranes. It was found that uniform incorporation of microporous MOF-801 with preferential CO2 adsorption provided fast and selective transport channels for CO2 over N-2, thereby achieving an increase both in CO2 permeance and CO2/N-2 mixed-gas selectivity compared with pure PEBA membrane. The optimized MOF-801/PEBA mixed-matrix composite membrane (MOF loading of 7.5 wt%) exhibited high and stable separation performance with CO2 permeance of 22.4 GPU and CO2/N-2 selectivity of 66 under mixed-gas permeation test, showing great potential for practical CO2 separation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据