APPLIED SURFACE SCIENCE
卷 369, 期 -, 页码 525-534出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.apsusc.2016.02.020
关键词
Thin film semiconductor; Galvanic synthesis; Photocatalytic property; Thermoelectric property
类别
资金
- University Grants Commission (India)
- Department of Science and Technology (DST), India [SR/S2/CMP-0031/2011]
Cu2-XSe thin film with cubic berzelianite phase was prepared by a simple, low-cost two electrode electrochemical technique and the photocatalytic and thermoelectric properties of the thin films were investigated. The results showed that Cu2-XSe crystallized in the cubic berzelianite phase and found to possess both direct and indirect band gaps of 2.9 and 1.05 eV respectively, covering almost the entire range of solar-spectrum. The photocatalytic discoloration of aqueous methylene blue (MB) and rose-bengal (RB) dyes over Cu2-XSe thin films were investigated under visible light irradiation. Cu2-XSe thin films showed higher catalytic activity for MB compared to RB in presence of H2O2. The photocatalytic discoloration followed first-order reaction kinetics. Complete removal of aqueous MB was realized after visible light irradiation for 150 min with Cu2-XSe thin film catalyst in presence of H2O2. Thermoelectric performances through power factor and figure of merit have been evaluated. Carrier concentration obtained from thermoelectric power was used to evaluate the mobility of carriers from electrical conductivity measurement. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据