Polymer degradation; Self-renewal polyurethane; Low surface energy; Antifouling coating
资金
- Analysis and Testing Center of Hainan University
- [zzzz002023317]
- [zzzz002023301]
Two polyurethanes were prepared through the reaction of 1,6-diisocyanatohexane (HDI) with two kinds of alcoholates. The first alcoholate was synthesized from alcoholized lactide (PLA) and dodecafluoroheptyl methacrylate (DFHMA) with the solid super acid (SO42-/ZrO) acting as the catalyst, and the other alcoholate was a mixture of PLA and DFHMA. The composition and structure of these two polyurethanes were investigated by infrared spectroscopy (FTIR) and differential scanning calorimetry (DSC). The mass loss, attachment of bacteria and algae, and the water contact angle were used to evaluate the degradable and antifouling performance of the two polyurethane coatings. The results showed that the maximum contact angle of PLIPFI reached 129 degrees, its mass loss was higher than 10% in 65days, and after 65days, the mass loss appeared to be stable, and the antiadhesion performance of the polyurethanes coatings was also enhanced. All of these results indicated that the PU modified with a graft segment may be promising for obtaining antifouling materials that not only can resist the adhesion of microorganisms but also show self-renewal. [GRAPHICS] .
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据