INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS
卷 81, 期 -, 页码 189-195出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijrmhm.2019.02.026
关键词
Ultrahigh temperature ceramics; Pressureless sintering; ZrB2; TiC; Graphite
In this research, the pressureless sintering of ZrB2 composites were studied to obtain the highest densification and investigate the effects of TiC (2-10% wt) and graphite (1-2% wt) additives on the sinterability. The results showed that by adding TiC, the porosity and water absorption of the samples decreased, resulting in an increase in the density of the samples up to similar to 98% of the theoretical density. The addition of graphite and TiC reduced the surface oxide layers, improved the density and prevented the grain growth. The graphite additive reacted with B2O3 and ZrO2 and allowed the system to achieve a complete densification at 2000 degrees C. Both TIC and graphite additives were completely consumed during the sintering process and the in-situ formation of TiB2 and ZrC phases were proved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据