关键词
GFRP-composites; Delamination; IR-thermography; Cohesive elements
Delamination is the major failure mechanism in composite laminates and eventually leads to material failure. An early-detection and a better understanding of this phenomenon, through non-destructive assessment, can provide a proper in situ repair and allow a better evaluation of its effects on residual strength of lightweight structural components. Here we adopt a joint numerical-experimental approach to study the effect of delamination on the fatigue life of glass/epoxy composites. To identify and monitor the evolution of the delamination during loading, we carried out stepwise cyclic tests coupled with IR-thermography on both undamaged and artificially-damaged samples. The outcome of the tests shows that IR-thermography is able to identify a threshold stress, named damage stress ?D, which is correlated to the damage initiation and the fatigue performance of the composite. Additionally, we performed FE-simulations, implementing the delamination by cohesive elements. Such models, calibrated on the basis of the experimental fatigue results, can provide a tool to assess the effect of parameters, such as the delamination size and location and composite stacking sequence, on the residual strength and fatigue life of the composite material.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据