CERAMICS INTERNATIONAL
卷 45, 期 16, 页码 20977-20982出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2019.06.249
关键词
HfB2-SiC ceramics; Multi-layered structure; Nb interlayer; Fracture toughness
资金
- National Natural Science Foundation of China [51632007, 51672218]
- National Key R&D Program of China [2017YFB1103500, 2017YFB1103501]
Herein, laminated HfB2-SiC/Nb ceramic with multi-layered structure was synthesized via tape casting and spark plasma sintering. Despite minor loss in strength of laminated HfB2-SiC/Nb ceramics (447 +/- 12 MPa) compared with that of monolithic HfB2-SiC ceramics (470 +/- 16 MPa) following the introduction of ductile weak Nb interlayer, fracture toughness of laminated ceramics reached 14.22 +/- 0.6 MPa m(1/2), showing an improvement of similar to 129% in comparison with monolithic ceramics (6.11 +/- 0.3 MPa m(1/2)). Cooperative toughening mechanisms of crack behavior (deflection and delamination) and plastic deformation (dimples and tear ridges) led to the improvement in toughness. This research provides novel strategy for the development of heterogeneous ceramic-metal layered composites with superior fracture toughness.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据