Reactivity of glasses is predominantly linked to the degree of depolymerization of the glass structure. In this work, eight calcium aluminosilicate glasses were synthesized with compositions reflecting the glassy phases of industrial fly ashes and slags. The chosen composition ranges allow for isolation and identification of the roles of Ca and Al. The reactivity of the glasses is found to be mainly dependent on the CaO content as calcium depolymerizes the glass structure and increases the rate of reaction of the glasses. The effect of Al2O3 on glass reactivity is less pronounced and relies on chemical weakening of the glass structure. However, an increasing alumina content has a pronounced effect on the hydrate phase assemblage, bound water content, portlandite consumption and the heat of reaction. The resulting compressive strength of composite cement mortars incorporating the synthesized CaO-Al2O3-SiO2 glasses is found to be a function of both the degree of glass reaction and the actual phase assemblage.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据