Template-free; Macro/mesoporous; Heterojunction; Visible light; g-C3N4/TiO2; Photocatalytic activity
资金
- National Natural Science Foundation of China [51302112]
Mesoporous photocatalytic materials with macroporous structures have attracted more and more attention because of their textural mesopores and intrinsic interconnected pore networks, which are able to efficiently transport guest species to framework binding sites. In this work, macro/mesoporous g-C3N4/TiO2 heterojunction photocatalysts were fabricated without templates or additives by a facile calcination method using tetrabutyl titanate and melamine as the feedstocks. Photocatalytic experiments of the as-prepared samples were measured by the photocatalytic oxidation degradation of RhB solution at room temperature under visible light irradiation. The results indicated that the melamine content in the precursors had an important influence on photocatalytic activity of the as-prepared samples. At the optimal loading content, the apparent reaction rate constant (k) was 47.8 x 10(-3) min(-1) for RhB degradation, exceeding that of pure TiO2 (6.6 x 10(-3) min(-1)) and g-C3N4 (15.2 x 10(-3) min(-1)) by factor of 7.2 and 3.1 respectively. The improved photocatalytic activity was attributed to high surface area and heterostructure formation of g-C3N4/TiO2 composites. The trapping experiment results showed that O-center dot(2)- and h(+) were main active species in the decomposition of RhB. A possible enhanced photocatalytic mechanism of g-C3N4/TiO2 heterojunction photocatalysts was proposed. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据