期刊
APPLIED CATALYSIS B-ENVIRONMENTAL
卷 183, 期 -, 页码 282-290出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.apcatb.2015.10.044
关键词
SCR of NO with NH3; V2O5; Potassium poisoning; Heteropoly acids
资金
- Energinet.dk through the PSO project [10521]
The influence of varying the V2O5 content (3-6 wt.%) was studied for the selective catalytic reduction (SCR) of nitrogen oxides by ammonia on heteropoly acid (HPA)- and tungsten oxide (WO3)-promoted V2O5/TiO2 catalysts. The SCR activity and alkali deactivation resistance of HPA-promoted V2O5/TiO2 catalysts was found to be much higher than for WO3- promoted catalysts. By increasing the vanadium content from 3 to 5 wt.% the catalysts displayed a two fold increase in activity at 225 degrees C and retained their initial activity after alkali doping at a molar K/V ratio of 0.181. Furthermore, the catalysts were characterized by N-2 physisorption, XRPD, NH3-TPD, H-2-TPR, Raman, FTIR and EPR spectroscopy to investigate the properties of the catalysts. XRPD, Raman and FTIR showed that promotion with 15 wt.% HPA does not cause V2O5 to be present in crystalline form, also at a loading of 5 wt.% V2O5. Hence, use of HPAs does not cause increased N2O formation or unselective oxidation of NH3. NH3-TPD showed that promotion by HPA instead of WO3 causes the catalysts to possess a higher number of acid sites, both in fresh and alkali poisoned form, which might explain their higher potassium tolerance. Ex-situ EPR spectroscopy revealed that HPA-promoted catalysts have higher V4+ /V-totai ratios than their WO3-promoted counterparts. H-2-TPR suggests that HPAs do not have a beneficial effect on the V5+-V3+ redox system, relative to WO3. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据