ACS APPLIED MATERIALS & INTERFACES
卷 11, 期 27, 页码 24659-24667出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.9b03481
关键词
double perovskites; X-ray photoelectron spectroscopy analysis; electrical conductivity; area-specific resistance; IT-SOFC anode materials
资金
- SERB [PDF/2016/002021]
Lanthanum (La3+)-doped double perovskites Sr2CoMoO6 (Sr2-xLaxCoMoO6, 0.00 <= x <= 0.03) were synthesized via the citrate-nitrate autocombustion route. The Reitveld refinement analysis of X-ray diffraction reveals the tetragonal symmetry as the main phase with space group I4/m and also confirms the presence of some peaks corresponding to extra phase SrMoO4. The SEM micrograph images reflect that grains are in irregular shape and sizes for all samples. Average grain size gradually decreases with the increase of the SrMoO4 phase. The X-ray photoelectron spectroscopy (XPS) analysis confirms the presence of mixed valence states of Mos(+)/Mo6+, Co2+/Co3+, and O-lattice/O-chemisorbed/O-physisorbed species. Coefficient of thermal expansion (CTE) analysis shows that the particular composition Sr1.97La0.03CoMoO6 has the lowest CTE value among the compositions studied. The electrical conductivity of Sr2CoMoO6 is enhanced effectively by doping La at Sr sites. The measured area-specific resistance (ASR) for the composition Sr1.97La0.03CoMoO6 (SLCM03) is found to be appreciably low, similar to 0.053 Ohm cm(-2) at 800 degrees C. The obtained highest electrical conductivity with the lowest activation energy and low ASR value for the composition Sr1.97La0.03CoMoO6 encompasses it as a promising candidate for anode material in the intermediate-temperature solid oxide fuel cell (IT-SOFC) application.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据