nickel-containing sludge; microwave; dielectric properties
资金
- Foundation of Henan Educational Committee [18A530002]
- Key Scientific and Technological Project of Henan Province [182102310896]
Permittivity is a vitally important parameter for the description of the absorption and heating characteristics of materials under microwave irradiation. In this paper, the permittivity of nickel-containing sludge (NCS), which is created during battery production as a cheap secondary resource, was measured at temperatures from 20 degrees C to 600 degrees C at 2.45 GHz using the cavity perturbation method. In addition, the loss tangent (tan) and penetration depth (Dp) of microwaves into the material were calculated. The results of the permittivity study show that the dielectric constant (epsilon) and dielectric loss factor (epsilon) of the NCS increase with increasing temperature. The variations of the loss tangent (tan) and penetration depth (Dp) with the temperature can be divided into two parts at 200 degrees C. The effect of the initial moisture content on the dielectric properties of the material is notably greater than that of the temperature, which was confirmed by the heating curve. After microwave pretreatment, the nickel-containing phase is transformed into NiO, while the weight of NCS is reduced by more than 20%, the particle size is significantly reduced and the leaching time reduce 20 min than that of conventional heating.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据