期刊
ADVANCES IN MATERIALS SCIENCE AND ENGINEERING
卷 2019, 期 -, 页码 -出版社
HINDAWI LTD
DOI: 10.1155/2019/2629464
关键词
-
资金
- Ministry of Education and Science of Ukraine under the project Controlled electrochemical synthesis of metal nanoparticles and nanostructured materials [0118U000268]
The process of gold nanoparticle (AuNP) precipitation on the silicon (Si) surface by galvanic replacement (GR) in dimethyl sulfoxide (DMSO) solution depending on the concentration of H[AuCl4], temperature, and duration was investigated. It is established that with an increase in the concentration of [AuCl4](-) ions (from 2 to 8mM H[AuCl4]), both the size of AuNPs and their surface coverage density are increased. It is demonstrated that an increase in temperature causes the size of AuNPs to increase from 40 to 80nm at 40 degrees C to 80-120 and 120-160nm at 50 and 60 degrees C, respectively. As the duration of the GR process increases, there is a tendency of the particle size growth. Under the studied deposition conditions, the organic aprotic solvent medium contributes to the formation of spherical AuNPs with 2D substrate filling. It is established that the AuNPs deposited on the silicon surface catalyze the process of metal-assisted chemical etching (MacEtch), which makes it possible to obtain Si nanostructures in the form of nanowire arrays.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据