ACS SUSTAINABLE CHEMISTRY & ENGINEERING
卷 7, 期 12, 页码 10661-10669出版社
AMER CHEMICAL SOC
DOI: 10.1021/acssuschemeng.9b01312
关键词
Lithium-ion battery; LiNi0.8Co0.15Al0.05O2; Doping; Cyclic performance; High cutoff voltage
资金
- Science & Technology Commission of Shanghai Municipality [08DZ2270500]
As a kind of Ni-rich cathode material, LiNi0.8Co0.15Al0.05O2 undergoes severe phase transition when cycling under a high cutoff voltage, causing a sharp decline in reversible capacity. In this study, we synthesize LiNi0.8Co0.15Al0.05O2 with a range of Ti doping contents through a facile solid state approach. When the doping content is 1 mol %, it can still deliver a discharge capacity of 179.6 mAh g(-1) after 200 cycles at 3.0-4.5 V, with a capacity retention of 97.4%, in comparison with 167.3 mAh g(-1) and 89.2%, respectively, for pristine Revealing the Effect of Ti Doping on Significantly Enhancing Cyclic Performance at a High Cutoff Voltage for Ni-Rich LiNi0.8Co0.15Al0.05O2. Various morphological and structural characterizations are performed to thoroughly comprehend the excellent cyclic performance of Ti-doped Revealing the Effect of Ti Doping on Significantly Enhancing Cyclic Performance at a High Cutoff Voltage for Ni-Rich LiNi0.8Co0.15Al0.05O2. High resolution transmission electron microscopy images in combination with powder X-ray diffraction patterns illustrate that Ti dopant effectively suppresses the undesirable phase transition. Electrochemical impedance spectroscopy results confirm a relatively low increase of charge transfer impedance, and differential capacity versus voltage curves show a more moderate polarization during cycling. When LiNi(0.8)Co(0.15)Al(0.05)O(2 )cycles under a high cutoff voltage, the appropriate amount of Ti doping plays a role in stabilizing the structure and relieving the surface deterioration, which proves to be the key to the extremely superior cyclic performance even at 4.5 V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据