期刊
SURFACE & COATINGS TECHNOLOGY
卷 374, 期 -, 页码 116-123出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2019.05.079
关键词
Inconel 625 alloy; Wire and arc additive manufacturing; Cold metal transfer; Microstructure; Mechanical properties
资金
- National Natural Science Foundation of China [51575401]
In the present study Inconel 625 alloy fabricated using Cold Metal Transfer (CMT) Wire Arc Additive Manufacturing (WAAM) has been investigated. The microstructure and mechanical properties of the fabricated Incone1625 alloy, and the influence of torch travel speed on the properties of the manufactured specimens were researched. Microstructural studies revealed variation in microstructure in different layers of the specimen, with the bottom layer consisting of fine primary cellular grains. Mechanical properties that include hardness and tensile properties showed that with the increase in the travel speed, average micro-hardness of the manufactured specimens slightly improved from 248 HV to 253 HV. The ultimate tensile strength (UTS) increased from 647 MPa to 687 MPa, while yield strength (YS) increased from 376 MPa to 400 MPa. Results showed that the mechanical performance of the manufactured components by CMT-WAAM method was better than the mechanical properties of Inconel 625 alloy casting parts except UTS, which demonstrated that the Inconel 625 alloys can be fabricated by cold metal transfer process.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据