期刊
RARE METALS
卷 39, 期 1, 页码 70-75出版社
NONFERROUS METALS SOC CHINA
DOI: 10.1007/s12598-019-01223-4
关键词
Permanent magnets; Low remanence temperature coefficient; Er doped; Magnetic performance characterization
Er-doped Sm1-xErx(CobalFe0.15Cu0.08Zr0.03)(7.8) (x = 0, 0.1, 0.2, 0.3) magnets with a low remanence temperature coefficient were prepared by powder metallurgy method. The influence of Er content on the remanence and microstructure was investigated. X-ray diffractometer (XRD) analysis showed that the magnets with different Er contents consist of 2:17R phase and 1:5H phase. Scanning electron microscopy (SEM) analysis showed that the composition of the matrix is consistent with stoichiometric composition and no obvious precipitated phase appears. With the increase in doped Er amount, the temperature stability of Sm1-xErx(CobalFe0.15Cu0.08Zr0.03)(7.8) (x = 0, 0.1, 0.2, 0.3) is getting better. When x is up to 0.3, the magnets with a low remanence temperature coefficient are obtained and the remanence descends tardily from 0.86 to 0.80 T as the temperature rises from room temperature to 400 degrees C. These results indicate that Er substitution for Sm in SmCo-based permanent magnets together with optimal composition and proper heat treatment could achieve a desired magnetic performance combined with high thermal stability.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据