期刊
MICROPOROUS AND MESOPOROUS MATERIALS
卷 278, 期 -, 页码 366-377出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.micromeso.2019.01.016
关键词
Oxidative glycerol dehydration; Acrylic acid; H,Fe-MCM-22 catalysts
类别
资金
- Fundacao de Apoio a Pesquisa do Estado da Bahia (FAPESB)
Gas-phase oxidative dehydration of glycerol to generate acrylic acid has been studied on bifunctional H,FeMCM-22 catalysts aiming at the use of glycerol obtained as co-product during transesterification of vegetable oils to produce biodiesel. In this work, MCM-22 zeolite was submitted to consecutive ion exchanged with Fe+ solutions for three times to obtain different iron loadings. The samples were calcined, characterized and evaluated in the gas-phase oxidative glycerol dehydration at 320 degrees C. The increase of iron content resulted in a decrease of acid sites density and textural properties. Fe3+ oligomers and iron oxide clusters were identified as the main iron species. The catalyst containing the lowest iron content has shown better activities and yields to acrylic acid. Higher glycerol conversion was favored by a balance between acid and textural properties. Acrylic acid yield increased with the reaction time, reaching 57% after 10 h on the catalyst containing 1.2 wt% of iron. These results suggest that H,Fe-MCM-22 are promising catalysts for a sustainable production of acrylic acid in substitution of vanadium based catalysts.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据