期刊
MATERIALS CHARACTERIZATION
卷 154, 期 -, 页码 169-180出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2019.05.022
关键词
Spark plasma sintering; High-entropy alloy; Phase; Texture; Mechanical properties
类别
资金
- National Key R&D Program of China [2017YFB0306305]
- National Natural Science Foundation of China [51874369, 51871249]
- Guizhou Science and the Technology Plan Project [GHK support [2017] 2013]
- Central South University
Spark plasma sintering (SPS), as a novel powder consolidation method, has great potential in the production of high entropy alloys (HEAs). The heating rate is an important parameter in SPS, and understanding its effect is a critical issue for the purpose to optimize microstructure and promote mechanical properties of HEAs. The AlCoCrFeNi was adopted as a representative HEA in this study. The phase compositions, microstructural textures, and mechanical properties were investigated in this study in detail. It was found that the FCC phase formed at BCC grain boundaries while the alpha phase precipitated at the interface of B2/BCC no matter of the heating rate. The texture varied at different heating rates as the texture {110} < 755 > in B2/BCC was characterized at the heating rate of 150 degrees C/min while the complex texture {051} < 715 > in FCC was observed at the heating rate of 200 degrees C/min. The Vickers hardness and wear resistance decreased with increasing of the heating rate. Furthermore, the compressive strength and corresponding plastic strain reached their highest 2752.0 +/- 48 MPa and 26.5 +/- 1.3% at the heating rate of 150 degrees C/min.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据