JOURNAL OF MATERIALS RESEARCH
卷 34, 期 10, 页码 1805-1817出版社
CAMBRIDGE UNIV PRESS
DOI: 10.1557/jmr.2019.153
关键词
composite; nanostructure; phase transformation
资金
- National Natural Science Foundation of China [51362003, 51762004]
- Key Research Project of Hunan Provincial Department of Education [17A145]
- Key Research Project of Xinjiang Agricultural and Vocational Technical college [XJNZYKJ201502]
A kind of n-p (SnO2)(1.3)/(alpha similar to Bi2O3)(x)/(beta similar to Bi2O3)(1-x) nanocomposite (SB-15) was synthesized with polyvinyl alcohol (PVA) as a template by solid state synthesis. XRD and HR-TEM confirmed the formation of n-p (SnO2)(1.3)/(alpha similar to Bi2O3)(x)/(beta similar to Bi2O3)(1-x). Particle size is found to be about 18 nm from HR-TEM images. FE-SEM clearly detected the boundary between SnO2 nanoparticles and Bi2O3 polyhedron particles. The special morphology and coexisting of alpha-Bi2O3 and beta-Bi2O3 in SB-15 make it have a stronger visible light absorption range as far as 725 nm. PL and photocurrent test shows that the SB-15 has the best photocarriers separation capability. About 99% decolorization ratio of Rh.B was achieved in only 5 min. About 70% Cr6+ was degraded within 20 min and it is about 60% for tetracycline in the coexisting system (Te with Cr6+ solution), introducing it as a promising photocatalytic material. This work has addressed the method of phase-selective synthesis of n-p SnO2/alpha similar to Bi2O3/beta similar to Bi2O3 by convenient solid state synthesis, which should be useful for the studies of other composites.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据