High entropy alloy; Solid-liquid interface; Directional solidification; Microstructure; Tensile properties
资金
- Fund of State Key Laboratory of Advanced Welding and Joining, the National Natural Science Foundation of China [51825401, 51741404]
In order to understand effect of solidification velocity on microstructure evolution and mechanical properties of high entropy alloys (HEAs), CoCrFeNi HEA samples were directionally solidified at different solidification velocities (5-50 mu m/s). The results show that all samples were directionally solidified, but the solid-liquid interface and columnar grains are different. Microstructure of them is only composed of FCC solid solution phase. Morphology of solid-liquid interface transforms from cellular, to cellular-dendritic, and then to dendritic with increasing of solidification rate. The criterion of solidification rate for cellular/dendrite transition is calculated as about 26.1 mu m/s based on experimental results. The width of columnar grains decreases from 200 mu m to 100 mu m with solidification rate increasing from 5 mu m/s to 50 mu m/s. Meanwhile, secondary dendrite spacing decreases from 200 mu m to 30 mu m for dendritic solidified samples (v = 10-50 mu m/s). Tensile testing show that the yield strength improves from 233 MPa to 383 MPa, and the ultimate tensile strength improves from 431 MPa to 596 MPa with increasing of solidification rate. Meanwhile, the elongation of all samples is more than 34.3%, but rupture morphology analysis shows that the rupture changes from quasi-cleavage fracture to ductility fracture. The improvement of tensile properties is resulted from grain boundary strengthening of the columnar grain and second dendrite. (C) 2019 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据