La1-xSrxVO3 (LSV)-based perovskite anodes are chemically and electrochemically stable under SOFC operating conditions. The main objective of this study was to investigate the feasibility of obtaining La0.7Sr0.3VO3 nanopowder from a novel hydrothermal method at relative low-temperature (similar to 200 degrees C). The particle size of hydrothermally-processed La0.7Sr0.3VO3 powder was as fine as 50 nm based on transmission electron microscopy observation. As a result, the better crystallization and densification was demonstrated from La0.7Sr0.3VO3 nanopowders synthesized via a hydrothermal route in comparison with a solid-state reaction (SSR) method. La0.7Sr0.3VO3 nanopowder shows a perovskite-type structure after heat-treated at 800 degrees C for 5 h in a reducing atmosphere (20% H-2, 80% Ar). The hydrothermally treated La0.7Sr0.3VO3 showed high density of 96% that is better than the SSR process (86%). La0.7Sr0.3VO3 synthesized by the hydrothermal process shows metallic conducting behavior. Its conductivity reached 193 s cm(-1) at 800 degrees C which is adequate for SOFC application. (c) 2019 The Japan Society of Applied Physics
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据