CORROSION SCIENCE
卷 156, 期 -, 页码 16-31出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2019.04.043
关键词
Stainless steel; Supercritical carbon dioxide; High-temperature corrosion; Oxide layer
资金
- Engineering Research Center Program of MSIP/NRF of Rep. of Korea [2016R1A5A1013919]
- Sichuan Science and Technology Program of P. R. of China [2018JY0155]
- BK-Plus Program of the MSIP/NRF of Rep. of Korea
- China Scholarship Council
The corrosion behavior of four stainless steels (SSs) with similar chromium content was investigated in supercritical carbon dioxide environment. Overall, weight gain was the smallest for 630 SS which formed thin and continuous Cr-rich oxide layer. Due to large Mn3O4 nodules, weight gain was larger for 430 SS. For 347H and 316LN SSs, thick duplex oxide layers were formed following the extensive oxide spallation, resulting in much greater weight gains than 430 and 630 SSs. The oxide spallation was explained by the formation of Nb-rich layer or amorphous matters at the matrix/oxide interface as well as the matrix structure.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据