ACS APPLIED MATERIALS & INTERFACES
卷 11, 期 22, 页码 20249-20256出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.9b03014
关键词
superlubricity; layered double hydroxide; nanoadditive; polyalkylene glycol; water-based; tribological properties
资金
- China Postdoc Innovation Talent Support Program [BX20180168]
- National Natural Science Foundation of China [51527901, 51875303]
- China Postdoctoral Science Foundation [2019M650654]
- Chinese Scholarship Council (CSC)
It was previously proved that the existence of a large amount of hydrogen ions in water-based lubricants can easily lead to a superlubric state; however, it was also shown that these hydrogen ions could cause severe corrosion. As part of a large family of attractive clays, layered double hydroxides (LDHs) possess excellent tribological properties in water-based lubrication systems. In the present work, two different kinds of LDHs are dispersed in polyalkylene glycol (PAG) aqueous solutions, in two distinct forms: ultrathin nanosheets (ULDH-NS) of ca. 60 nm wide and ca. 1 nm thick (single or double layer) and nanoparticles (LDH-NP) of ca. 19.73 nm wide and ca. 8.68 nm thick. We find that the addition of ULDH-NS greatly shortens (as much as 85%) the running-in period prior to reaching the superlubricity regime and increases the ultimate load-bearing capacity by about four times. As compared to the fluid film thickness of the lubricating PAG solution, their ultrathin longitudinal dimension will not impair or influence the fluid film coverage in the contact zone. The analysis of sliding solid surfaces and the atomic force microscope microscale friction test demonstrate that the adsorption of ULDH-NS enables the sliding solid surfaces to be polished and protected because of their relatively weak interlayer interaction and increased adhesion effect. Owing to their superior tribological properties as lubricant additives, ultrathin LDH nanosheets hold great potential for enabling liquid superlubricity in industrial applications in the future.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据