Chalcogenide glasses; Ac conductivity; Dielectric relaxation; CBH model; Activation energy
资金
- UGCDAE-CSR Indore, India
Amorphous Ge10-xSe60Te30Inx(0 <= x <= 6) chalcogenide glasses were prepared by melt quench technique. Surface morphology with the chemical composition of the prepared glass was examined using SEM and EDS analysis respectively. Dielectric properties and a.c. conductivity of the multicomponent Ge10-xSe60Te30Inx(0 <= x <= 6) chalcogenide glasses have been examined in the frequency range 100 Hz-1 MHz and temperature range 303-328 K. It was noticed that dielectric constant and dielectric loss decreases with the increase of frequency and increases with the increase of temperatures. Frequency and temperature dependence of dielectric constant was explained by orientational polarization. The variation of dielectric loss with frequency and temperature was explained by conduction loss and theory of single polaron hopping of charge carriers suggested by Elliot and Shimakawa for chalcogenide glasses. The experimental results show that a.c. conductivity follows the power law omega(s) where s < 1 and value of s decreases with the increase of temperature. The present findings of a.c. conductivity and variation of s with temperatures are reasonably well interpreted in terms of CBH model.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据