期刊
MATERIALS RESEARCH EXPRESS
卷 6, 期 5, 页码 -出版社
IOP PUBLISHING LTD
DOI: 10.1088/2053-1591/ab0226
关键词
hierarchical rutile/anatase TiO2; electrodeposition; BiOI; visible absorption; charge carrier separation
资金
- National Key Research and Development Project [2016YFC0202402]
- National Natural Science Foundation of China (NSFC) [41675126, 51502143, 51472123]
Bismuth oxyiodide (BiOI) modified rutile/anatase TiO2 heterostructure was fabricated by a three-step process. Anatase TiO2 sheet was first formed on fluorine-doped tin oxide (FTO) glass substrate. Rutile TiO2 nanorods were then grown on anatase TiO2 sheet via a hydrothermal process. BiOI was finally coated on the surface of hierarchical TiO2 film using an electrochemical deposition method. Photocatalytic tests on degradation of methylene blue (MB) in water indicated that BiOI modified hierarchical TiO2 film possessed an excellent photocatalytic activity superior to those of the monophase anatase and rutile TiO2 films, commercial P25 film and hierarchical anatase/rutile TiO2 film. The enhanced photocatalytic performance was probably attributed to the synergetic effects of strong visible light absorption and formation of heterojunctions by the interfaces in the BiOI/rutile TiO2/anatase TiO2/FTO structure, which promoted efficient separation of photoinduced electronhole pairs. In addition, the main active species during the degradation were confirmed to be hydroxyl radicals and superoxide radicals.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据