Al-Zn-Mg-Cu; isothermal compression; recrystallization; recrystallization mechanism
资金
- National Basic Research Program of China [2017YFB0306301]
- National Natural Science Foundation of China [51705539]
Fine-grained (average gain size 3.8 mu m) and coarse-grained (average gain size 24.9 mu m) Al-Zn-Mg-Cu alloys were subjected to isothermal compression at 10(-3) s(-1) and temperature ranges from 300 degrees C to 450 degrees C. The grain structures after isothermal compression were observed by electron backscatter diffraction (EBSD). The results show that the continuous dynamic recrystallization (CDRX) mechanism dominated to form sub-grains in grain interiors during isothermal compression of coarse-grained materials, and sub-grains were gradually developed in grain interiors as the effective strain increased. Discontinuous dynamic recrystallization (DDRX) was the main recrystallization mechanism during isothermal compression of fine-grained materials, in which finer recrystallized grains were formed at grain boundaries. The temperature of isothermal compression had little influence on the recrystallization when the growth of recrystallized grains was slight, and sub-grains were hardly developed in fine-grain interiors.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据