期刊
AIP ADVANCES
卷 9, 期 3, 页码 -出版社
AIP Publishing
DOI: 10.1063/1.5079394
关键词
-
资金
- In-House Laboratory Independent Research (ILIR) program for the Force Protection Program of the Office of Naval Research [0602123N]
In this work, we investigate the effects of substituting Ni/Al for Cr on the thermomagnetic and magnetocaloric properties of FeCoNiCrAl-type high entropy alloys (HEAs). Ni and Al appear to prefer the BCC phase, and increases in the Al composition appear to stabilize the BCC phase. In contrast to Al, Ni content yields an increase in the FCC phase fraction, resulting in a drop off in magnetization. The phase transformation from BCC to FCC was intensified at annealing temperatures of 800 degrees C and higher due to increased diffusion rates and the resulting spinodal decomposition. A magnetic phase transition around 150 K was found in the FeCoNi1.5Cr0.5Al annealed alloy potentially corresponding to the FCC phase, and a very broad magnetic phase transition was observed in the annealed FeCoNiCrAl alloy, resulting in a high refrigerant capacity of RCFWHM = 242.6 J.kg(-1) near room temperature. A peak magnetic entropy change of -Delta S-M = 0.674 J.kg(-l).K-1 was also obtained at applied fields of similar to 70 kOe at 290 K in the FeCoNiCrAl HEA. These magnetocaloric values are comparable to Fe-based metallic glasses such as Fe-Tm-B-Nb and Fe-Zr-B-Co alloys, with a similar transition near room temperature. (C) 2019 Author(s).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据