Electrical Heating Performance of Electro-Conductive Para-aramid Knit Manufactured by Dip-Coating in a Graphene/Waterborne Polyurethane Composite

期刊

SCIENTIFIC REPORTS
卷 9, 期 -, 页码 -

出版社

NATURE PUBLISHING GROUP
DOI: 10.1038/s41598-018-37455-0

关键词

-

资金

  1. Basic Science Research Program through the National Research of Korea (NRF) - Ministry of Science, ICT and Future Planning [NRF-2016M3A7B4910552]

向作者/读者索取更多资源

An electro-conductive para-aramid knit was manufactured by a dip-coating in a graphene/waterborne polyurethane(WPU) composite for confirming to use as a fabric heating element applicable to a protective clothing requiring durability. The para-aramid knit was dipped in 8 wt% graphene/WPU composite solution up to five-coat cycles. As a result of electro-conductive textile by number of dip-coating cycles, the electrical, and specifically electrical heating performances were increased number of cycles from one to five. The sample with the best electrical and electrical heating performance was the five-coat sample, and to improve those properties it was hot-pressed at 100 degrees C, 120 degrees C, 140 degrees C and 160 degrees C. After hot pressing, the entire surface of the sample was filled with graphene/WPU composite and indicated smoothly surface, thus the electrical and electrical heating performance was improved than the five-coat sample. The best performance of was indicated hot-pressed at 140 degrees C, with a surface resistivity and capacitance of 7.5 x 10(4) Omega/sq and 89.4 pF, respectively. When a voltage of 50 V was applied, the surface temperature reached 54.8 degrees C. The five-coat sample with hot-pressed at 140 degrees C could be applied to a heat-resistant para-aramid knit glove with the touch screen of a mobile phone and electric heating performance.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据