Upgrading of Iron Concentrate by Fluidized-Bed Magnetizing Roasting of Siderite to Magnetite in CO-H2-N2 Atmosphere

Efficient use of abundant low-grade siderite ores can potentially mitigate the shortage of iron ore in the iron and steel industry in China. In this work, the beneficiation of siderite fines containing high levels of carbonates was studied using a combined fluidized-bed magnetizing roasting process. The siderite was almost completely converted into magnetite under the optimum conditions of preheating at 550 degrees C for 30s followed by magnetizing roasting at 550 degrees C for 60s at 0.5m/s gas fluidization velocity in a 13.3% CO+6.7% H-2+80% N-2 atmosphere. Magnetic separation was optimized using a fineness of that grind of 89.2% of the material passing 0.074mm and magnetic field intensity 0.2T. Comparative trials confirmed that the enhanced measures proposed, including optimizing gas fluidization velocity, preheating of the materials, the use of a mixed reducing gas, and selection of the optimum particle size of raw materials, could improve beneficiation of siderite. A high-grade magnetic concentrate containing 62.6wt% iron grade with an iron recovery of 89.2% was achieved. The results demonstrated an effective process to utilize siderite ores.